Industrial Heating, Volym 25National Industrial Publishing Company, 1958 |
Från bokens innehåll
Resultat 1-3 av 9
Sida 842
... cermet , made from ZrSiO , and aluminum powder , de- veloped a tensile strength of 5000 psi and reached 18,000 psi ... Cermets " , by B. C. Weber , P. E. Rem- pes , and M. A. Schwartz , Wright Air Development Center , Wright - Patter ...
... cermet , made from ZrSiO , and aluminum powder , de- veloped a tensile strength of 5000 psi and reached 18,000 psi ... Cermets " , by B. C. Weber , P. E. Rem- pes , and M. A. Schwartz , Wright Air Development Center , Wright - Patter ...
Sida 844
... cermet . The charpy impact resist- ance at room temperature increased with increase in the amount of metal reinforcement . The impact resistance of a 60Ni , 36TiC , 4 ( Ti , Ta , CbC ) cermet was increased by nickel plating . Plating ...
... cermet . The charpy impact resist- ance at room temperature increased with increase in the amount of metal reinforcement . The impact resistance of a 60Ni , 36TiC , 4 ( Ti , Ta , CbC ) cermet was increased by nickel plating . Plating ...
Sida 846
... cermet it was recommended that the torsion test should be included in the testing program for it is a simple test for determining the shear properties of a cermet . Test specimens were 6 % " long with 1 " square ends , and a 24 " long ...
... cermet it was recommended that the torsion test should be included in the testing program for it is a simple test for determining the shear properties of a cermet . Test specimens were 6 % " long with 1 " square ends , and a 24 " long ...
Innehåll
No | 31 |
Metallurgical Summary of 1957 By William H Eisenman | 40 |
III By C E Peck | 66 |
19 andra avsnitt visas inte
Andra upplagor - Visa alla
Vanliga ord och fraser
Ajax alloy aluminum annealing applications atmosphere automatic blast blower brazing brick Bulletin burner carbon carburizing cast castable ceramic chamber Chicago Cleveland coating coil combustion COMPANY complete continuous conveyor cooling copper Corp corrosion cost cycle Detroit Electric electrode Engineering fired fuel gases H. K. Porter hafnium hardening hearth furnace heat treating heaters high temperature inch Inconel induction Induction Heating INDUSTRIAL FURNACES INDUSTRIAL HEATING installation instrument insulation load machine manufacturer material ment metal Mineral wool mold motor nace nickel nozzles Ohio open hearth furnace operation oven oxide oxygen perature Phone Pittsburgh plant potentiometer pressure production pump pyrometer quench radiant tube range refractory resistance retort salt bath sintering stainless steel standard strip surface switch Taconite Harbor tank temperature control tempering thermal thermocouple tion ture unit vacuum valve Waukee wire Write zirconium zone