Industrial Heating, Volym 25National Industrial Publishing Company, 1959 |
Från bokens innehåll
Resultat 1-3 av 66
Sida 1536
... copper on the top of a pre - sintered iron part and passing the assembly through a furnace at 2100 ° F . At this temperature the copper readily melts and soaks into the pores of the iron part . Source of hydrogen atmosphere , usually ...
... copper on the top of a pre - sintered iron part and passing the assembly through a furnace at 2100 ° F . At this temperature the copper readily melts and soaks into the pores of the iron part . Source of hydrogen atmosphere , usually ...
Sida 2254
... copper . To melt the copper , and have it suf- ficiently liquid to form a good joint , the assembly must be heated to a temperature of about 2000 ° F . Intricately shaped parts that will not be subjected to any appre- ciable stresses or ...
... copper . To melt the copper , and have it suf- ficiently liquid to form a good joint , the assembly must be heated to a temperature of about 2000 ° F . Intricately shaped parts that will not be subjected to any appre- ciable stresses or ...
Sida 2548
... Copper and Silver Brazing of Metal , Metallic Oxide Reduction , Melting Metals , Powdered Metal Sin- tering and Bright Annealing of Metals . PIH The double - end , through - type fur- nace is designed for copper and silver brazing of ...
... Copper and Silver Brazing of Metal , Metallic Oxide Reduction , Melting Metals , Powdered Metal Sin- tering and Bright Annealing of Metals . PIH The double - end , through - type fur- nace is designed for copper and silver brazing of ...
Innehåll
JULY | 1321 |
Consumable Electrode Vacuum Arc Melting Furnace | 1338 |
in Flexible Installation | 1349 |
10 andra avsnitt visas inte
Andra upplagor - Visa alla
Vanliga ord och fraser
Ajax alloy aluminum ammonia annealing applications atmosphere automatic blast furnace Blower brazing brick Bulletin capacity carbon carburizing cast castable Catalog chamber Chicago Cleveland coating coils combustion Company complete conveyor cooling Corp corrosion cost cycle Detroit dew point drying efficiency Electric electrode endothermic ENGINEERING equipment exothermic ferromanganese FIRE BRICK firing flame fuel gas burners gases GLOBAR graphite hardening heat treating heaters high temperature hour hydrogen Inconel INDUCTION Induction Heating INDUSTRIAL FURNACES Industrial Heating installation insulating iron kiln Lindberg load machine manufacturer material melting ment metal motor nace Ohio operation oven oxide oxygen paint perature Phone Pittsburgh plant pressure production pumps Pyrometers quench radiant tubes range refractory resistance retort salt bath sintering soaking steel surface tank tempera temperature thermal Thermocouple tion ture unit vacuum valve Waukee wire Write zone