... Zirconium had an effect similar to titanium in that the grain - coarsen- ing temperature at first increased rapidly ... zirconium additions . MEAN OF GRAIN COARSENING RANGE 1800 1700 600 1500 0 02 04 06 08 10 12 4 J6 % ZIRCONIUM Fig . 8 ...
... Zirconium had an effect similar to titanium in that the grain - coarsen- ing temperature at first increased rapidly ... zirconium additions . MEAN OF GRAIN COARSENING RANGE 1800 1700 600 1500 0 02 04 06 08 10 12 4 J6 % ZIRCONIUM Fig . 8 ...
Sida 256
... Zirconium had very little effect on mechanical properties ( Fig . 8 ) . Increasing zirconium additions caused a progressive improvement in impact properties , especially in lowering the temperature of brittle fracture , despite the ...
... Zirconium had very little effect on mechanical properties ( Fig . 8 ) . Increasing zirconium additions caused a progressive improvement in impact properties , especially in lowering the temperature of brittle fracture , despite the ...
Sida 402
... zirconium , columbium , molybdenum , tantalum , tungsten- might be expected to stabilize cementite if it can fit into the structure . The experimental data , in so far as they go , confirm predictions made on the basis of the structure ...
... zirconium , columbium , molybdenum , tantalum , tungsten- might be expected to stabilize cementite if it can fit into the structure . The experimental data , in so far as they go , confirm predictions made on the basis of the structure ...
Innehåll
JANUARY 1947 No 1 | 25 |
HULTGREN Salt Bath Furnaces are widely | 27 |
Ma | 35 |
29 andra avsnitt visas inte
Andra upplagor - Visa alla
Vanliga ord och fraser
alloy aluminum annealing applications atmosphere automatically controlled bath blast furnace Bldg brazing brick Bulletin carbon carburizing cast Catalog cementite charge chemical Chicago chromium Cleveland coating combustion COMPANY complete construction cooling Corp decarburization Detroit diameter door drying electric engineering equipment FIRE BRICK fired flame fuel gas-fired gases handling hardening HEAT TREATING heater heating chamber high temperature hot face Inconel induction Induction Heating INDUSTRIAL FURNACES INDUSTRIAL HEATING infra-red ingot installation instrument insulation iron leadwire liquid load machine magnesia manufacturer material melting ment metal method mold motor nace Ohio OIL BURNERS Open Hearth open-hearth furnace operation OVENS oxide perature pits Pittsburgh plant plastic potentiometer pressure production pyrometer radiation range Refractory Concrete salt-bath slag steel STREET CHICAGO strength surface tempera temperature temperature control thermocouple tion tube ture unit valve wall welding wire