... carbonitriding , covers the process . The second article will discuss the constitution of carbonitrided cases . The Carbonitriding Process of Case Hardening Steel By G. W. P. RENGSTORFF , M. B. BEVER , and C. F. FLOE The first paper ...
... carbonitriding , covers the process . The second article will discuss the constitution of carbonitrided cases . The Carbonitriding Process of Case Hardening Steel By G. W. P. RENGSTORFF , M. B. BEVER , and C. F. FLOE The first paper ...
Sida 2052
... carbonitriding furnace was varied to observe the effect on the case formed . No difference in structure or hardness was found and comparable case depth to the samples carbonitrided in " dry " gases resulted . This indicated that wide ...
... carbonitriding furnace was varied to observe the effect on the case formed . No difference in structure or hardness was found and comparable case depth to the samples carbonitrided in " dry " gases resulted . This indicated that wide ...
Sida 2122
... carbonitriding temperature was raised . The specimen carbonitrid- ed at 1300 deg . F contained almost 2.5 % carbon on the surface , the specimens carbonitrided at 1400 deg . F contained over 3.0 % carbon and the specimens carbonitrided ...
... carbonitriding temperature was raised . The specimen carbonitrid- ed at 1300 deg . F contained almost 2.5 % carbon on the surface , the specimens carbonitrided at 1400 deg . F contained over 3.0 % carbon and the specimens carbonitrided ...
Innehåll
INDUSTRIAL | 1142 |
Worlds Largest Induction Furnace for Aluminum Melting in Operation | 1150 |
Removing Fine Particles from High Temperature Industrial Stack | 1160 |
26 andra avsnitt visas inte
Andra upplagor - Visa alla
Vanliga ord och fraser
alloy aluminum American annealing applications atmosphere automatic baking blast blast furnace gas Blast Gates blower brazing brick Bulletin carbon carbonitriding carburizing cast chemical Chicago Cleveland combustion COMPANY complete conveyor cooling core corrosion cost Detroit Division dryer drying ENGINEERING equipment finishing fired flame forging foundry fuel fumes gas burners gases GLOBAR hardening heat treating high temperature Inconel Induction Heating Industrial Furnaces Industrial Heating installation Instrument insulation iron load machine manufacturer material ment metal metallurgical method MICHIANA Micromax Misco mold nace Ohio OIL BURNERS Open Hearth Open Hearth Furnaces operation oven oxide perature Pittsburgh Pittsburgh 19 plant pressure production Pyrometer quench recirculating refractory Republic Steel Corp requirements resistance roller speed steam Steel Corp supply surface tank Tempering thermocouple tion tray tube ture unit valve welded wire Write